Robustness of Self-Compacting Geopolymer Concrete (SCGC)

Robustness of Self-Compacting Geopolymer Concrete

Warren Mc Kenzie, Technical Manager, BASF Construction Chemicals, Dubai, U.A.E

It’s widely known and has been reported on numerous occasions and in multiple journals that concrete is one of the most used construction materials in the world. With current cement production in excess of 2.8 billion tonnes globally it is forecast to exceed four billion tonnes year on year. [1] The production of OPC contributes to greenhouse gasses, in the form of CO2. Latest reports indicate the 0.6 to 0.8 kg of CO2 is emitted per 1 kg of OPC produced. The net result: CO2 contributes to approximately 65% of global warming. The cement industry is the third largest contributor, responsible for approximately 5 - 6% of CO2. [1][2]

Despite the numerous uses and benefits of concrete OPC remains the primary source of binder in conventional concrete. The production of which consumes vast quantities of energy while simultaneously depleting quarried resources. However, these concerns remain a secondary concern compared to the volume of CO2 produced as a result of the calcination process. Through the implementation of sustainable developments within the civil engineering society, the use of materials with lower environmental impact have gained traction. This has led to the acceptance, use and specification of materials such as PFa, GGBS, MS, etc.

Based on their characteristic properties, pozzolanic and/or hydraulic, these materials are considered to be either secondary or supplementary materials. Replacement of OPC with PFa and GGBS are generally minimal, however research has shown that high levels of replacement are possible. Recently it has been reported that environmentally friendly concrete can be produced by replacing OPC with materials such as PFa and GGBS and activating them using a high alkali solution(s). This process is affectionately referred to/identified as AAM or Geopolymer concrete, a term coined by French Prof. Davidovits. [3][4]

Geopolymer concrete provides a sustainable, environmentally friendly alternative to OPC based concrete by reducing CO2 emission by up to 45% while remaining economically competitive. [1] These reductions are often looked at only as operational CO2 (oCO2) and not as the embodied carbon dioxide (eCO2), which can be defined as the emissions derived from the construction and disposal phase in terms of the element’s life cycle. Geopolymer concrete has been successfully deployed in countries such as Australia. The next progressional step in the evolution of concrete technology is a truly revolutionary material, Self-Compacting Geopolymer Concrete (SCGC). [5][6] SCGS is in a situation similar to what conventional Portland cement based self-compacting concrete (SCC) was, where despite the numerous benefits associated with SCC such as improved durability, improved production rate/output, reduction of repairs reduced or reallocation of labour etc. the sensitivity and robustness of the mix remains questionable and unproven. [7][8][9]

Scope
Most studies on geopolymer concrete have focused on the reaction kinetics of the polymerization process rather than the development and understanding of a concrete that can be introduced into the industry, with a limited number of studies focusing on concrete as opposed to mortar mixes. Review of literature shows that the focus has been on molarity of the activator and the Al/Si ratio with little regard to the complexities of preparing a mix design, one that is robust enough to tolerate variation in water content. The term “robustness” is open to interpretation in the industry as there are various definitions of robustness for concrete. For example, RILEM TC 288 MPS classifies robustness as “the characteristic of a mixture that encompasses its tolerance to variation in constituent characteristics and quantities, variations during concrete mixing, transport, and placement, as well as environmental conditions”. [10] While the European Guidelines defines robustness as “the capacity of concrete to retain its fresh properties when small variations in the property’s quantities of the constituent materials occur”. [11] To investigate the robustness the mixing water was decreased by 5 l/m3 (3.57%) and 10 l/m3 (7.14%) or increase by 5 l/m3 (3.57%) and 10 l/ m3 (7.14%), presenting with a total variation of 20 l/m3 (14.28%).

Fly Ash Based Geopolymer
A conceptual model of the polymerization of aluminosilicates using alkaline activationFigure 1: A conceptual model of the polymerization of aluminosilicates using alkaline activation
The reaction between highly concentrated aqueous alkali solutions and binders, consisting predominantly of silicon (Si) and aluminium (Al), produces a synthetic alkali aluminosilicate material often referred to as geopolymer, a term Davidovits used to emphasize greater polymerization. [3][4][12] However, this reaction of an inorganic polymer has also been referred to as low-temperature aluminosilicate glass [13], inorganic polymer concrete [14], alkali-activated cement [15], and alkali-activated material, resulting in confusion globally as to how we identify this breakthrough technology correctly.

This process is affectionately referred to/identified as geopolymer concrete or alkali-activated material (AAM). Going forward the term geopolymer will be used as it is preferred by most researchers and the industry. The typical geopolymerization process of Figure 1, [14] provides a very general and linear illustration of the different phases in the polymerization process while Figure 2, illustrates different poly(sialate) structures formed as a result of the different Si:Al ratios. [15] The term poly(sialate) is a chemical designation of geopolymer based on silica-aluminates, where the sialate is the abbreviation for silicon-oxo-aluminate and the alkali may be either sodium (Na+), potassium (K+), lithium (Li+) or calcium (Ca2+). [12] Polysialates range from amorphous to semi-crystalline three-dimensional silica-aluminate structures and are chain and ring polymers with Si4+ and Al3+ in a IV fold coordination with oxygen. The accepted formula of polysiliates is; Mn(-(SiO2)z-AlO2)n.wH2O, where (M) is a cation and (n) is a degree of poly condensation.

To have successful polymerization, the formation of a (Mz(AlO2)x(SiO2)y.nMOH.H2O) gel is critical and a regarded as a dominant step in the geopolymerization process.

Ground-Granulated Blastfurnace Slag Based Geopolymer
Factors effecting the strength development of geopolymer with GGBS as the primary source of binder are: the type and dosage of alkaline activator, the means of adding said activator, the type and fineness of binder, ratio of SiO2:Na2O, curing temperatures and water:binder ratio. [16] The reaction of GGBS based geopolymer is different from that of PFa. The latent hydraulic GGBS main component is the development of calcium silicate hydrate (C-S-H) gel along with aluminium resulting in calcium silicate hydrate with aluminium gel (C-A-S-H), similar to the C-S-H formed by OPC based concretes. [17] The C-A-S-H formed through alkali activation has a Ca:Si ratio below 1.5 whereas the Ca:Si ratio of OPC based concrete is approximately 2.0. [12][18][19]

Poly(sialates) structures of geopolymer as per DavidovitsFigure 2: Poly(sialates) structures of geopolymer as per Davidovits
The high calcium content along with the low aluminium content of GGBS changes the mechanism of alkali activation compared to PFa, where the cation (R+) acts as a catalyst in the initial phases of hydration via cationic exchange with the Ca2+ ions during the early stages of hydration and strength development as per Figure 3. They are then combined into the structure forming zeolite-like phases. [12][18] The use of alkali hydroxides, sodium being the most common, play multiple roles in the hydration process. During the hydration phase of GGBS, in both OPC and geopolymer systems, a coating forms on the slag particles which in turn prevents further hydration. In cement based systems the hydration of the Ca(OH)2 maintains an alkaline environment which is required to break this coating allowing continuous hydration. Similarly, the alkali hydroxide provides and maintains the supply of OH- anions in the system ensuring the coating breaks down. [12][20]

The hydration process is effected by the sodium content and the Ca:Si ratio and begins with the destruction of the slag bonds Ca-O, Mg-O, Si-O-Si, Al-O-A and Al-O-Si before a Si-Al layer is formed of the binder prior to the formation of the hydration products as per Figure 3.

A series of reactions in the activation process of GGBSFigure 3: A series of reactions in the activation process of GGBS

The nature and composition of products formed during the activation of GGBS remain controversial and require continuous research. Most research conclude and accept the following assertions: [18]
  • The main hydration product is a composition of calcium silicate hydrate with aluminium (C-A-S-H gel) with a Ca:Si ratio less than 1.5;
  • The structure and composition of the C-A-S-H gel is dependent on the type and amount of activator used.
The presence of aluminium results in a gel forming long linear chains, as well as, the possible existence of sporadic inter-chain Si-O-Al bonds consequently forming two-dimensional cross-linked structures. Figure 4 shows that under these conditions the C-S-H gel would become a C-(A)-S-H gel. The type of activators used, being either silicate or hydroxide based, has a direct effect on the degree of silicate species condensation in the gel structure, with sodium silicate presenting with highly condensed structures. It was noted that the use of sodium hydroxide to activate the GGBS results in tetrahedral aluminium in bridging positions of the silicate chains. [18]

C-A-S-H formation based on NaOHFigure 4: C-A-S-H formation based on NaOH

Sodium Hydroxide
NaOH more commonly known as caustic soda or lye is produced via electrolysis. Three types of electrolytic cells are used, Castner-Kellner cells (Mercury process), Nelson diaphragm cells and membrane cells. The preferred method is shown in Figure 2.30 and discussed further below. [21] The membrane cell method is favoured for the production of NaOH; it has a low energy demand to produce pure NaOH with no hazardous waste. The cell consists of a two-compartment system with a titanium anode, nickel cathode and an ion-exchange membrane separating the anode from the cathode. Saturated brine solution enters the anode compartment where oxidation takes places releasing chlorine gas, 2Cl-(aq) => Cl2(g) + 2e-. The depleted brine is removed and replaced in a continuous process. [21]

The membrane selectively allows Na+ and water to migrate from the anode compartment to the cathode compartment where the solution reacting with the cathode releases hydrogen, 2H2O(i) + 2e => H2(g) + 2OH-(aq).

The Na+ combines with the OH- to form a concentrated NaOH, 2H2O(i) + 2Cl-(aq) + 2Na+(aq) => 2Na+(aq) + 2OH-(aq) + H2(g) + Cl2(g). Solid NaOH is obtained by the evaporation of this solution.[68]

Molarity
The concentration of the solution is referred to as molarity and is defined as the number of moles of solute per liter of solution. The molarity of NaOH is calculated where molarity is compared to moles in solute. The relationship between activator molarity and the performance (compressive strength) of geopolymer concrete has been studied. Geopolymer produced using a molarity of 14 showed significant increase in compressive strength while mixes produced with 18 mole showed marginal decrease in compressive strength. It has been observed that increasing the molarity of the activator leads to better results. [22][23][24]

Several reports have been made regarding the dosage of activator; however, they remain inconsistent. For example, geopolymer prepared with NaOH within the range of 1-10% by mass of binder reported that the higher the dosage, the better the strength; other reports indicate the variation of dosage within the range of 3-11% had little effect on the strength. [25]

Wang reports that to increase the molarity in combination with the dosage of activator, defined as the ratio between Na2O in the activator and binder as a percentage, has a significant influence on the compressive strength. [25][26]

It’s reported that the optimum Na2O dosage for GGBS based geopolymer is between 3-6%, based on early strength requirements and the type of GGBS used. However, the Na2O value varies according to total binder volumes as illustrated in Table 2.9 whereby the activator dosage remains constant at 25l/m3 and the total binder ranges from 300 kg/m3 to 500 kg/m3.

Molarity in the case of NaOH is limited to a maximum of approximately 19 mole per litre as NaOH solidifies at 20°C at a concentration of 52% by mass. [85] Therefore a solution of approximately 18 mole (M) NaOH was prepared by dissolving NaOH flakes in water to achieve an approximate 50% mass fraction (w/w). Several trials were conducted using various levels of NaOH before settling on a value as per the proposed mix design. Laboratory trials indicated a strong correlation to results found in research, showing that there appears to be an optimum dosage for the activator.

Literature has revealed that increasing the molarity of activators has a negative effect on plastic properties such as slump-flow, v-funnel and slump-flow t-500 times; yet a positive effect on compressive strength. [6][27][28][29][30][31][12][13]

With the primary focus being on the molarity of the activator(s), the effect of free water has been erroneously disregarded. Numbers, in the first row of Table 1, taken from [29] illustrate the focus on molarity; not taking into account the change of free water as the dosage of activator remains consistent, depicted in the rows that follow. Table 1 provides a breakdown of total water by calculating the solid content of NaOH at various molarities from a theoretical mix while Figure 5 illustrates the effect of free water on compressive strength.

The effect of free water on compressive strengthFigure 5: The effect of free water on compressive strength

Table 1, Breakdown of total water by calculating NaOH solid content at various molarities from a theoretical mix design
Binder Coarse Aggregate Fine Aggregate Molarity NaOH Activator Active NaOH (kg/m3) Free Water (kg/m3) Water (12% of Binder) Total Water in Mix (kg/m3)
425 935 830   210     51  
      1   6.4 201.6   252.6
      2   16.8 193.2   244.2
      4   33.6 176.4   227.4
      8   67.2 142.8   193.8
      16   134.4 75.6   126.6

Super Plasticizers
Commercial superplasticizers such as lignosulphonate, sulphonate naphthalene formaldehyde, sulphonate melamine formaldehyde and polycarboxylate ether, used in OPC based concretes, have been well documented in literature. The use of these constituents has become common practice as they adhere onto the cement surface, often building up multiple layers on individual grains, whereby they deflocculate and disperse the agglomerated cement particles through the following mechanisms: electrostatic repulsion, reduction of the surface tension of water and steric hinderance, releasing the entrapped water and increasing fluidification. [32][33]

The charge of both cement and superplasticizers is recorded as zeta potentials, which is the function of the charge of the particles with absorbed polymers. Therefore, it should be noted that OPC is positively charged to approximately +10 mV as a result of the multi-phase dissolution of the silanol phases. Superplasticizers, with a negative zeta potential, endeavour to reduce the positive zeta potential in the system. By cancelling one another out, the superplasticizers become absorbed onto the cement grain. Despite the latest generation superplasticizers having a zeta potential of -5 to -10 mV they are rendered useless in the high alkaline environment of geopolymer and provide little to no improvement in workability; however, they may compromise the set time and compressive strength by as much as 50%. [34][35]

Conventional PCE’s consist of an anionic backbone which attracts counter ions resulting in the neutralization of their anionic charge and therefore influencing their adsorption characteristics. The presence of cations and the amount found within the pore solution blocks the negative charges resulting in a reduction of adsorption onto the binder and therefore provides minimal plasticizing properties. [15]

BASF Construction Chemicals have developed a superplasticizing admixture for use in geopolymer concrete. However, the intellectual property of the admixture is protected by patents and other commercialization processes therefore the properties of the admixture will not be discussed or disclosed.

Mix Design
Progression of mix proportioning between CVC, SCC and SCGCFigure 6: Progression of mix proportioning between CVC, SCC and SCGC
Multiple studies have shown particle packing principles (PPP), also known as particle packing models (PPMs), which take into account particle shape, size and distribution to improve the performance of concrete by reducing porosity and is an essential step in the mix design phase. PPP can be applied to most concretes, however, there are a few notable differences between conventional vibrated concrete (CVC) and SCC, some more important than others, while SCGC is not dissimilar to SCC.

Both SCC and SCGC require a higher paste content compared CVC and is achieved by the manipulation of the aggregate proportions, binder content and total water content. Figure 6 shows the progression of mix proportions form CVC to SCC to SCGC. Reducing the ratio of coarse aggregate to fine aggregate adds stability to the mix, although it may be necessary to substitute the largest aggregate for one size down; i.e., 20 mm to 10 mm.

A well-designed thixotropic SCC/SCGC should be able to resist dynamic segregation in the fluid state yet reduce the lateral stress on the formwork i.e. hydrostatic pressure. Once the concrete comes to a rest, the fluid structure can restore the yield stress and prevents further dynamic, segregation a phenomenon resulting from flocculation. [36][37]

Based on PPP and the conceptual models shown, a theoretical mix design, Table 2, has been developed to meet the guidelines, as set out by BS EN 206:2013 and EFNARC. [38][39]
Table 2, Theoretically proposed mix design
Raw Material Kg/m3 % m3 eCO2 Dry vs Liquid % Aggregate vs Mix % Coarse vs Fine vs Liquid %
20mm Stone 380 11.76 3.53 91.60 73.95 29.62
10mm Stone 425 7.85
Crusher Sand 680 28.57 3.78 61.97
Dune Sand 375 15.76
GGBS 375 15.76 19.50 26.05
MS 45 1.89 0.63
Water 140 5.88 0.14 8.40 8.40
Admixture 35 1.47 0.35
NaOH 25 1.05 28.75
 
Theoretical Total 2 380 100.00 0.024 100.00 100.00 100.00

Curing
It is thought that geopolymer concrete produced utilizing conventional and well-established curing procedures will add further confirmation regarding the robustness of the mix.

Curing of conventional concrete has been described as “the maintenance of appropriate moisture and temperature conditions to permit the continuation of the hydration or pozzolanic reaction”. The “hydration” phase of geopolymer concrete is more of a polymerization phase than an actual hydration phase as is the case in conventional concrete where CSH is formed. It is thought that geopolymer concrete produced with a basic GGBS will have a minimal calcium content and could be considered as self-curing, where no water curing is required.

Evaluation of Plastic Properties
In an effort to ensure a harmonious and representative evaluation of each test characteristic, concrete used for a single test is returned to the pan where it was manually mixed by hand prior to moving onto the next test method, i.e. following the completion of the mixing sequence the slump-flow and slump-flow t500 were recorded. The concrete was then returned to the pan and using a scoop, the concrete was mixed by hand to form a representative sample before conducting the J-ring test. The procedure followed for evaluation of the plastic properties was based on the ergonomics of the laboratory and were: slump flow and slump-flow t500, J-ring, V-funnel, plastic viscosity and finally sieve segregation. After which all concrete was returned to the mixer and covered with polythene to measure slump retention

Slump Flow
The slump-flow values of the various mixes highlight the direct effect water has on workability. The slump-flow decreases in a near linear trajectory as the mixing water is reduced; while slump-flow increases, as water content increases, in a more parabolic trajectory, indicating that further increases in water content would cause segregation and thus reduce the slump-flow values as depicted in Figure 7 and Figure 8. As per BS EN 206:2013 the concrete is classed as SF3.

Slump-flow line chart summary of the effect various water contents have at T= 0, T= 30, T= 60, and T=90 minutesFigure 7: Slump-flow line chart summary of the effect various water contents have at T= 0, T= 30, T= 60, and T=90 minutes

Xbar chart summary of the effect various water contents have at T= 0, T= 30, T= 60, and T=90 minutes on slump-flowFigure 8: Xbar chart summary of the effect various water contents have at T= 0, T= 30, T= 60, and T=90 minutes on slump-flow

Plastic Viscosity
The results recorded from the plastic viscosity measurement are reported as Pa.S in Table 3. Analysing the box plot Figure 9, the histogram Figure 10, it is noted the that the plastic viscosity increases as the water content decreases and visa versa as the plastic viscosity decreases as the total water content is increased as per figure 11. These results follow the notion that variation in water has a direct effect on plastic viscosity as a result of the relationship between stress and rate of strain.

Plastic viscosity box plot reference mix with water contents decreased and increased by 5 and 10 litres respectivelyFigure 9: Plastic viscosity box plot reference mix with water contents decreased and increased by 5 and 10 litres respectively

Plastic viscosity histogram reference mix with water contents decreased and increased by 5 and 10 litres respectivelyFigure 10: Plastic viscosity histogram reference mix with water contents decreased and increased by 5 and 10 litres respectively

Table 3, Plastic viscosity values (Pa.S) reference mix with water contents decreased and increased by 5 and 10 litres respectively
Plastic Viscosity Reference Mix -5 Ltr Water Mix -10 Ltr Water Mix +5 Ltr Water Mix +10 Ltr Water Mix
Repeat 1 38.9 55.5 54.8 26.7 24.4
Repeat 2 38.4 54.2 63.7 39.5 29.5
Repeat 3 58.8 39.5 52.3 27.7 28.6
Repeat 4 38.5 38.1 41.4 29.0 28.5
Repeat 5 40.4 45.0 62.7 41.2 32.8
Repeat 6 33.3 62.6 71.9 35.1 28.1
Repeat 7 27.5 55.2 68.2 34.6 28.0

Plastic viscosity values compared to average slump-flow values for reference mix with water contents decreased and increased by 5 and 10 litres respectivelyFigure 11: Plastic viscosity values compared to average slump-flow values for reference mix with water contents decreased and increased by 5 and 10 litres respectively

Compressive Strength
The strength development of test specimens remain consistent despite being subjected to different curing methods. The strength development between mixes is shown in Figure 12, providing a clear illustration of the strength development trend. Figures 1, 2, 3, 4, 5 in Appendix 3 provide a direct comparison between water cured and air cured specimens per mix design. These results are also shown in Tables 1, 2, 3, 4, 5, 6, 7, 8, 9 and 10 in Appendix 3. Specimens cured in the stability chamber demonstrated that the water curing was not a requirement to ensure the geopolymerization process continues. Furthermore, the continuous strength development indicates that this process had not concluded and that higher strengths could be expected at later ages.

Strength development of water cured vs air curedFigure 12: Strength development of water cured vs air cured

The influence of the water content on the compressive strength suggests the water:binder ratio is a critical factor in the production of geopolymer concrete. Following extensive research into activation of geopolymer concrete, molarity can be regarded as a critical factor regarding the success of the mix. It has also been noted that molarity is only ever considered as a value of the activator and not of the total mix design. It is therefore proposed that the active molarity of activator and subsequently the active Na2O be used for a more accurate calculation in the development of geopolymer concrete. In other words, a mix design using 250 l/ m3 water and 50 l/ m3 of 18 M sodium hydroxide has an active / effective molarity of 0.126 in a m3. Using a superplasticizer to reduce the water content by 100 litres increases the active/effective molarity to 0.189 in a m3, an improvement of more than 65%.

Summary
The results of the investigation into both plastic and hardened properties, as well as curing, can be summarized as follows:
  1. Geopolymer produced using GGBS blended with MS presents with acceptable performance properties and therefore validates the replacement of 100% OPC.
  2. The use of exciting test methods were used in accordance with the appropriate method except where highlighted and discussed.
  3. Changes in water content had a direct effect on the plastic properties. However, evidence suggests that the changes in plastic properties were subtle, proving the concrete was able to tolerate the variance without segregation.
  4. The decrease in water content had the greatest effect on the pass-ability of the v-funnel and the plastic viscosity.
  5. The strength development of the various mixes was not affected by the curing procedures/methodologies. However, the compressive strength is related to the water content of the mix and not the Na2O as previously reported.
  6. While the methods of curing had minimal effect on compressive strength, the specimens subjected to air curing presented with improved performance properties with regard to RCPT and water absorption. The low water absorption can be attributed to a dense matrix as a result of the fineness of the GGBS and thus compliments the chloride resistance properties of geopolymer producing a longer service life.
  7. The porosity of the concrete represented by the low water absorption values are attributed to the high fineness and irregular shape of the GGBS. Both the high fineness and irregular shape increase the surface area and therefore increased the reaction between the binder and activator.
  8. The improved chloride diffusion rate results from the low porosity of the concrete. However, it is noted that the concentration of NaOH increases the chloride binding capacity of the concrete thereby providing a dual action system for the reduction of chloride ingress.
  9. The saturated capillaries result in polymerization around the capillariesFigure 13: The saturated capillaries result in polymerization around the capillaries
    While all initial results indicate geopolymer produced with GGBS and MS provide acceptable compressive strength and improved durability results, the long-term performance properties require further examination in order to be validated.
  10. It is theorized that the compromised performance properties of hardened properties subjected to water curing is a result of excess water interfering with the polymerization process as illustrated in Figure 13, with saturated capillaries forcing the polymerization to wrap around the capillary; while Figure 14 illustrates how the C-A-S-H gel may cross through the capillary thereby changing and limiting the absorption properties.
  11. Although this interference is negligible for compressive strength, it is thought that in the absence of excess water, the C-A-S-H gel is allowed to form through the capillaries thereby providing a denser matrix and improving the overall durability of the concrete.
C-A-S-H gel polymerizes through the empty capillariesFigure 14: C-A-S-H gel polymerizes through the empty capillaries

Conclusion
This chapter presents the main conclusions which can be drawn following the investigation into the robustness of SCGC to changes in water content and the effect curing has on the hardened properties of the various mixes.

Analysis of the results from this study present the following conclusions:
  1. The results confirm SCGC is robust enough to tolerate changes in water content without segregation, contrary to its reputation of being sensitive to change in moisture.
  2. The study found that SCGC is repeatable across a range of tests, in both the plastic and hardened states.
  3. Changes in plastic properties remain intuitive, whereby the increase or decrease of water has the desired/expected result.
  4. The results derived from air curing are counter intuitive and produced improved durability results. This finding introduces the industry to a unique advantage over conventional concrete, with further cost saving possibility as a result of/in a reduction of curing cost.
  5. SCGC may be regarded as state of the art in the continuous progression to improve concrete quality and extend service life of structures. However, there remains much work needed till we achieve an understanding similar to that of conventional concrete.
  6. The primary hydration product is amorphous and comprised of C-A-S-H gel.
  7. All mix designs remained within the limits set out by EN BS 206:2013, despite some variation from one classification to another.
  8. The mix design proportions and understanding of how they interact in a holistic manner is a primary step to ensure a robust mix design is produced.
  9. The strength development of geopolymer is a complex multi-stage process, which is affected by several components such as water:binder ratio, Si:Al ratios, activator types and dosage, the percentage of Na2O per binder, as well as, the total free molarity.
  10. Despite changes to the curing methodology geopolymer demonstrates suitable performance characteristics for harsh conditions, such as marine environments where there is a need to resist the ingress of chlorides.
  11. In general, both plastic and hardened properties have successfully demonstrated acceptable performance in the short term. The evaluation of these properties needs to be evaluated to understand the long-term characteristics, insuring there is no relapse of performance at a later stage.
  12. The use of standard/common test methods proved suitable for the evaluation of the selected properties, however there is a requirement to standardize test procedures for geopolymer concrete, particularly if the specimens are air cured; i.e. drying shrinkage, the specimens may have a higher shrinkage rate initially, however as the capillaries are filled as a result of polymerization the shrinkage value may be lower than that of a water cured specimen.
References
  1. Gunaseera, C. Setunge, S and Law, D.W. 2018. Creep and drying shrinkage of different fly-ash-based geopolymers. ACI Materials Journal V116 No.1 pp. 39-49
  2. Rangan V B. 2014. Geopolymer concrete for environmental protection. The Indian Concrete Journal, Vol. 88, Issue 4, pp. 41-59
  3. Davidovits J. 1982, The Need To Create A New Technical Langue For The Transfer Of Basic Scientific Information, Published In Transfer And Exploration Of Scientific and Technical Information, Commission Of The Wuropoean Communities, Luxembourg, 1982, pp, 316-320
  4. Islam. A, Alngaram. U. J, Jumaat. M. Z and Bashar. I. I. 2014, The Development Of Compressive Strength Of Ground Granulated Blast Furnace Slag-Palm Oil Fuel Ash-Fly Based Geopolymer Mortar. Materials And Design, 56. Pp 833-841.
  5. Geopolymer Concrete, Z16 recommended practice. 2011. Available from: https://www.concreteinstitute.com.au/OnlineStore/Recommended-Practices/Geopolymer-Concrete
  6. Henigal A.M, Sherif M.A and Hassa N.N, 2017, Study On Properties Of Self-Compacting Geopolymer Concrete. Journal Of Mechanical And Civil Engineering, Volume 14, Issue 2, pp. 52-66.
  7. Roberts J, 2012. Sensitivity That Self-Compacting Concrete Shows Towards Repeatability In Rocla’s Precast Environment. Cape Peninsula University Of Technology
  8. Ghoddousi P. and Salehi, A, M. 2017, The Robustness Of Self-Consolidating Concrete Due To Changes In Mixing Water. PeriodicaPolytechnica Civil Engineering, 61(2), pp. 216 - 225
  9. Krishnamoorthy K. Some Major Issues Of Self-Compacting Concrete, Annamalai University, India. [Accessed 05 January 2019] Available from: https://www.icevirtuallibrary.com/doi/pdf/ 10.1680/rocisd.32477.0047
  10. De Schutter. G and Khayat. K. H, STAR 228-MPS, Mechanical Properties Of Self- Compacting Concrete. [accessed 16 February 2019] Available Online from: copyhttp://www.springer.com/engineering/civil+engineering/book/978-3-319-03244-3
  11. BS EN 206:2013, Concrete - Specification, Performance, Production And Conformity.
  12. Warhono, A. 2015, The durability of Fly Ash Geopolymer and Alkali-Activated Slag Concrete, School of Civil Environmental and Chemical Engineering, RMIT, pp. 1-222
  13. Van Mele H.R, BiesemansM, Wu J,W,X. 1996. Low-Temperature Synthesized Aluminosilicate Glasses, Journal Of Material Science, 31, pp. 71-79
  14. Duxson P, Fernandez-Jimenez, Provis. J.L, Lukey G.C, Palomo A, Van Deventer J,S. J. 2007, Geopolymer Technology: The Current State Of The Art. Journal Of Material Science, 42 pp. 2917-2933.
  15. Li C, Sun H, Li L. 2010. A Review: The Comparison Between Alkali-Activated Slag (Si+Ca) And Metakaolin (Si+Al) Cements. Cement And Concrete Research 40, pp. 1341-1349.
  16. Rovnaanik, P. 2010. Effect Of Curing Temperature On The Development Of Hard Structure Of Metakaolin-Based Geopolymer. Construction And Building Materials. 24, pp.1176 - 1183.
  17. Suresh, D and Nagaaju, K, 2105, Ground Granulated Blast Slag (GGBS) in Concrete - A Review. Journal of Mechanical and cCivil Engineering, Volume 12 Issue 4, pp. 76-82
  18. Garcia-Lodeiro.I, Palomo.A and Fernandez-Jimenez. A, An Overview of the Chemistry of Alkali-Activated Cement Based Binders. In: Handbook of Alkali-activated Cements, Mortars and Concretes. Woodhead Publishing Series in Civil and Structural Engineering:Number 54, pp. 33-40
  19. Beushausen H. 2009 Self-compacting Concrete. In: Owens, J. Edition 9. Fulton’s Concrete Technology. Midrand, South Africa: Cement And Concrete Institute, pp. 317-327
  20. Taylor. H.F.W. 1997, Cement Chemistry 2nd Edition. Chapter 7 pp. 187-225
  21. Sodium Hydroxide and Chlorine production by Electrolysis, [Accessed 08 July 2019] Available Online from: https://www.ausetute.com.au/chloralkali.html
  22. Abdullah. M. M. A, Kamarudin. H, Mohmmd. H, Hhairul Nizar. I, Rafza. A.R and Zarina.Y. 2011, The relationship of NaOH Molarity, Na2SiO3/NaOH Ratio, Fly Ash/Alkaline Activator Ratio and Curing Temperature to the Strength of Fly Ash-Based Geopolymer. Advanced Materials Research Vols. 328-330 pp. 1475-1482.
  23. Kabir. S.M.A, Alengaram. J.U, Jumaat. M.Z, Sharmin.A and Islam. Azizul, 2015, Influence of Molarity and Chemical Composition on the Development of Compressive Strength in POFA Based Geopolymer Mortar. Advances in Materials Science and Engineering, Volume 2015 Article ID 647071.
  24. Madheswan.C.K, Gnanasundar.G and Gopalakrishnan.N, 2013. Effect of Molarity in Geopolymer Concrete. International Journal of Civil and Structural Engineering Volume 4, No.2. pp. 106-115
  25. Wang. S, Scrivener. K.L and Pratt.P.L. 1993. Factors Affecting the Strength of Alkali-Activated Slag. Cement and Concrete Research. Vol. 24, No.6. pp. 1033-1043.
  26. Adam. A.A, 2009. Strength And Durability Properties Of Alkali-Activated Slag And Fly Ash- Based Geopolymer Concrete. School of Civil, Environmental And Chemical Engineering RMIT University, Melbourne. pp.25
  27. Taylor. H.F.W. 1997, Cement Chemistry 2nd Edition. Chapter 9 pp. 261-293
  28. Adam. A.A, 2009. Strength And Durability Properties Of Alkali-Activated Slag And Fly Ash-Based Geopolymer Concrete. School of Civil, Environmental And Chemical Engineering RMIT University, Melbourne. pp.4
  29. BS EN 450-1:2005+A1:2007, Fly Ash for Concrete - Part 1: Definition, specifications and Conformity Criteria.
  30. Jackson, P.J, Portland cement: Classification and Manufacture. In: Lea’s Chemistry of cement and concrete 4th edition, pp. 26
  31. Northwestern University, the science of concrete. [accessed 15 June 2019] Available on line from: http://iti.northwestern.edu/cement/monograph/monograph5_1.html
  32. Ramachandran V.S., Malhotra V.M, Jolicoer C. &Spiratos N.1998. Superplasticizers: Properties and applications in concrete pp. 59
  33. Zingg. A, Winnefeld. F, Holzer. L, Pakusch. J, Becker. S and Gaukelr. L. 2008. Adsorption of polyelectrolytes and its influence of rheology, zeta potential and microstructure of various cement and hydrate phases, Journal of Colloid and Interface Science 323 pp. 301 - 312
  34. Kong, D, L, K. and Sanjayan, J, G. 2010. Effect Of Elevated Temperatures On Geopolymer Paste, Mortar and Concrete. Cement And Concrete Research. 40, pp. 334-339.
  35. Edmeads.R.M and Hewlett. P.C, Cement Admixtures. In: Lea’s Chemistry of cement and concrete 4th edition, pp. 853
  36. Trgger. N, Gregori. A, Ferrara. L and Shah. S. 2012. Correlating Dynamic Segregation of Self-Consolidating Concrete to the Slump-Flow Test, Construction and Building Materials, 28, pp. 499 – 505
  37. Ovarlez G and Roussel. N. 2006. A Physical Model for the Prediction of Lateral Stress Exerted by Self-Compacting Concrete on Formwork. Materials and Structures, Volume 39, pp. 269 - 279
  38. BS EN 206:2013, Concrete - Specification, Performance, Production And Conformity.
  39. EFNARC, The European Guidelines For Self-Compacting Concrete, 2005, www.efnarc.org
About author
Warren Mc Kenzie is a Concrete Technologist and R&D specialist with 10 years’ experience in the industry. He graduated from the University of Leeds, UK, with MSc in civil engineering – specializing in advanced concrete technology. He has focused on topics such as 3D printing and Geopolymer concrete, becoming internationally recognized for his work on the later. He is currently the Technical Manager for BASF Construction Chemical for the Gulf States.

NBM&CW May 2020

Click Here
To Know More / Contact The Manufacturer
Please fill in your details, we will contact you as soon as possible
Choose Title from the listPlease let us know your name.
Please let us know your Designation.
Invalid Input
Please let us know your email address.
Please let us know your City.
Please let us know your Contact Number.
Please brief your query.
Our other value-added services:

To receive updates through e-mail on Products, New Technologies & Equipment, please select the Product Category(s) you are interested in and click 'Submit'. This will help you save time plus you will get the best price quotations from many manufacturers, which you can then evaluate and negotiate.

Equipment & Machinery
Invalid Input
Building Products
Invalid Input

Mechanical Properties of Geopolymer Concrete with Alternative Materials

Concrete is considered the world’s most versatile, durable and reliable construction material, next only to water. It is the most consumed material requiring large quantity of cement, fine aggregates, course aggregates Read More ...

Ferro-Sialate Geopolymer using Red Mud

Geopolymer is being used as a replacement for Portland cement for over the past three decades. The technology utilizes material rich in silica and alumina, either processed geological material or industrial byproducts Read More ...

Geopolymer Concrete - The Eco Friendly Alternate to Concrete

The name geopolymer was given by “Joseph Davidovits” in 1978. Geopolymer concrete (GPC) is an eco friendly product which uses industrial waste by-products such as fly ash (waste from thermal power plants) and ground Read More ...

Compressive strength study of Geopolymer Mortar using quarry rock dust

T. Venu Madhav, Head Department of Civil Engineering, Audisankara College of Engineering & Technology, Gudur, Andhra Pradesh, India. I.V. Ramana Reddy, Professor, Department of Civil Engineering, S.V.U. College of Engineering Read More ...

Use of Factory Made Reaction Generating Liquid (RGL - SRGPJ1) to Produce Geopolymer Concretes

Geopolymer binders, formed by alkaline activation of aluminosilicate precursors, are attracting interest as “green” cements because of their use of industrial wastes such as geothermal silicas, fly ashes and mineralogical Read More ...

Performance Evaluation of Fly ash and GGBFS Blended Self-compacting geopolymer concrete

An attempt has been made to develop Fly ash (FA) and Ground granulated blast furnace slag (GGBFS) blended self-compacting geopolymer concrete mixes with varying volume of pastes using conventionally available river sand Read More ...

Recent Developments in Concrete Technology

Recently, two new developments in concrete technology can have a far reaching impact on the way we consume concrete in construction. Concrete happens to be the largest in terms of weight—being about more than 5 tonnes per capita Read More ...

Green Products from the House of JSW Cement

"Through our wide range of future-ready, superior quality green products, we meet the evolving demands of the construction industry in India," avers Lopamudra Sengupta, Vice President (Technical services) JSW cement Read More ...

Sensitivity Analysis of Cable Profile of Prestressed Concrete Beams

The cable profiles for post-tensioning of concrete beams are usually designed as parabolic curves based on the eccentricity of the midpoint of the duct to the neutral axis of the beam. The end points and the midpoint of a duct are very important Read More ...

Overview of Concrete Ingredients, Concrete Mixes and Durability Requirements in Arabian Peninsula

Arabian Peninsula usually has either a tropical or subtropical arid desert climate or arid steppe climate. Arabian Desert - the great desert region in the extreme southwestern Asia - occupies almost the entire Arabian Peninsula. Read More ...

Industry 4.0 in Construction 3D Printing

The discovery of fire has generally been considered as the first and most significant discovery of mankind. Millenia and four industrial revolutions later, humanity has forged ahead and shown no signs of slowing down the scientific and technical Read More ...

Sustainability of Concrete Using Copper Slag as Replacement for River Sand

Concrete consumption is so extensive that it stands second to water. Spiraling urbanization has led to excessive consumption of concrete, which has increased the demand for sand, cement and coarse aggregates. The sand consumption across Read More ...

GGBFS Replacement for High Early Strength Concrete for Precast Industry

The Precast Concrete industry is one of the thriving industries in the wake of faster development with high quality standards. The initial capital cost for precast construction is higher than for conventional concrete. The chief requirement Read More ...

Simple Guidelines for Producing Sustainable, Durable and Economical Concrete

There is a dire need to control environmental pollution across the world. Concrete is a must for infra development. Cement, which is the main binding material for concrete, adds CO2 to the environment. At present 7.4% of CO2 is contributed Read More ...

Design & Construction of Composite Structures

Arun Nadig, Director, Nadig Consulting, presents two award-winning projects in composite construction technique for modern office spaces, which have been duly recognised by the Construction Industry Development Council (CIDC) for Read More ...

Self Concrete Mixer: AJAX Soaring Up New Heights!

AJAX, a world-class leader in providing concreting business solutions, was established in 1992 for manufacturing Self-Loading Concrete Mixers. Today, it is positioned as a global leader in this product category. Over the years Read More ...
NBM&CW

New Building Material & Construction World

New Building Material & Construction World
MGS Architecture

Modern Green Structures & Architecture

Modern Green Structures & Architecture
L&ST

Lifting & Specialized Transport

Lifting & Specialized Transport
II&TW

Indian Infrastructure & Tenders Week

Indian Infrastructure & Tenders Week