Improvement of Shear Strength using Triangular Shape Fibre in Concrete

    Prof. Priti A. Patel, Research Scholar in SVNIT and Asst. Prof. in CKPCET, Dr. Atul K. Desai, Associate Prof. and Head AMD, SVNIT, Dr. Jatin A. Desai, Retd. Prof. AMD SVNIT, Surat.

    It is now well established that one of the important properties of fibre reinforced concrete is its superior resistance to cracking and crack propagation. As a result of this ability to arrest cracks, fibre composites possess increased extensibility and tensile strength, both at first crack and at ultimate, particular under flexural loading; and the fibres are able to hold the matrix together even after extensive cracking. The net result of all these is to impart to the fibre composite pronounced post – cracking ductility which is unheard of in ordinary concrete. The transformation from a brittle to a ductile type of material would increase substantially & the energy absorption characteristics of the fibre composite and its ability to withstand repeatedly applied, shock or impact loading. In this paper, the mechanical properties of triangular shape polyester fibre, and applications of FRC are discussed.

    Introduction

    Fibre reinforced concrete (FRC) may be defined as a composite material made with Portland cement, aggregate and incorporating discrete discontinuous fibres. Why would we add such fibres to concrete? Plain, unreinforced concrete is a brittle material with a low tensile strength and a low strain capacity. The role of randomly distributed discontinuous fibres is to bridge across the cracks that develop & provide some post- cracking "ductility". If the fibres are sufficiently strong, sufficiently bonded to material, and permit the FRC to carry significant stresses over a relatively large strain capacity in the post-cracking stage.

    There are of course, other ways of increasing the strength of concrete. The real contribution of the fibres is to increase the toughness of the concrete (defined as some function of the area under the load vs. deflection curve), under any type of loading. That is, the fibres tend to increase the strain at peak load, and provide a great deal of energy absorption in post-peak portion of the load vs. deflection curve [4].

    When the fibre reinforcement is in the form of short discrete fibres, they act effectively as rigid inclusions in the concrete matrix. Physically, they have thus the same order of magnitude as aggregate inclusions; fibre reinforcement cannot therefore be regarded as a direct replacement of longitudinal reinforcement in reinforced and prestressed structural members. However, because of the inherent material properties of fibre concrete, the presence of fibres in the body of the concrete or the provision of a tensile skin of fibre concrete can be expected to improve the resistance of conventionally reinforced structural members to cracking, deflection and other serviceability conditions.

    The fibre reinforcement may be used in the form of three – dimensionally randomly distributed fibres throughout the structural member when the added advantages of the fibre to shear resistance and crack control can be further utilised. On the other hand, the fibre concrete may also be used as a tensile skin to cover the steel reinforcement when a more efficient two – dimensional orientation of the fibres could be obtained.

    Improvement of Shear Strength using Triangular Shape Fibre in Concrete
    Figure 1: Tensile Load versus Deformation for Plain and Fibre Reinforced Concrete

    The behavior of FRC under loading can be understood from Figure 1. The plain concrete structure cracks into two pieces when the structure is subjected to the peak tensile load and cannot withstand further load or deformation. The fibre reinforced concrete structure cracks at the same peak tensile load, but does not separate and can maintain a load to very large deformations. The area under the curve shows the energy absorbed by the FRCs when subjected to tensile load. This can be termed as the post cracking response of the FRCs. The real advantage of adding fibers is when fibers bridge these cracks and undergo pullout process, such that the deformation can continue only with the further input of energy from the loading source.

    Importance of Fibre Reinforced Concrete in Shear

    Shear failure in concrete is known to be brittle and catastrophic [8]. In usual structural design, shear is accounted for by providing shear reinforcement such as stirrups in beams. Sometimes the shear reinforcement may be less than sufficient if the loading configuration were different from that predicted during design, such as during earthquake or at critical section reinforcement conjunctions. Fibres are effective shear reinforcement, its increased shear strength and ultimately results in ductile flexure failures [7].

    If RC structure designed according to IS: 13290 (Code for ductile detailing), heavy reinforcement detailing will be in confinement zone of beam and column. If shear stress enhance by the addition of "Triangle Polyester Fibre" in the concrete, then stirrups spacing in structural component will be increased. Polyester fibre reinforces concrete satisfying ductility, durability and energy absorption criteria of RC structures. PFRC (Polyester Fibre Reinforced Concrete) also give high resistance to CO2, water and atmospheric gases in "cover zone" and protect reinforcement from corrosion. Polyester fibres in cover zone provide mechanism of "crack arrester" under earthquake, reversible cyclic, dynamic, and wind cyclonic load. Recently in IS: 456 in august 2007, some amendment was made for addition of "fibre" in concrete.

    Shear strength of fibre reinforced concrete plays very important role in construction of P.Q.C. (Pavement Quality Concrete) for road and at present in Surat in construction of road no steel reinforcements are used only "Triangle Polyester Fibre" are added for flexural shear of road. Steel doweling bars are used only at joints of road panel in longitudinal and lateral directions. Due to triangle shape of fibres in concrete gives more damping property. Ordinary concrete gives 5% damping, while TPFRC gives 6.5% damping and ultimately reduces dynamic loading on structure [6].

    In the most advanced and most recent design method, the contribution of fibre reinforcement to shear is completely ignored. Also no Indian design codes allow a reduction or removal of stirrups or dowels from beams, column and beam-column joint. Now a days, these techniques slowly entering into field, provide properties that are easily obtainable through fibre reinforcement.

    Research Significance

    FRC as a material is emerging from laboratory testing to field applications like in new construction, repair, retrofitting, etc. Structural characteristics should be understood properly for this ductile composite to be used in wide spectrum of applications. An attempt is, therefore, made in the present experimental investigation to analyses these composites, and to predict their performance in various loading conditions.

    Test Programme
    Material and Mixtures

    The mixture proportions and properties of concrete used in the test program are given in Table 1.

    Improvement of Shear Strength using Triangular Shape Fibre in Concrete

    OPC 53 grade cement, aggregate – maximum size of 9.5 mm and 19 mm, river sand and potable water were used. Super plasticizer – 140 ml/bag was used to achieve adequate fibre dispersion and workability. Polyester fibre (Recron 3S) of length 12mm were used as they exhibit good bond with cement being substantial triangular in cross section and offer better dispersion in the matrix being silicon coated. Variable: Fibre volume fraction – 0%, 0.5%, 1%, 1.5% and 2 %. From each mixture, the following specimens were cast: three cubes (150x150x150mm), cylinders (150mm dia. and 300 mm height), beams (100x100x500mm), L- shape specimen for shear (Refer fig 2.) Specimens will be test at 7 and 28 days.

    JSCE-SF6 suggested direct shear method by using beam of size (150x 150x 500 mm) and load applied through male–female arrangement and failure under double shear. Another method suggested by Dr. C.D. Modhera and Dr. N. K. Bairagi,[1] arrangement for which is shown in fig. 2.

    Improvement of Shear Strength using Triangular Shape Fibre in Concrete
    All Dimensions are in mm.
    Figure 2: Arrangement of Specimen for Shear Strength

    Results and Discussion
    Properties of Fresh Concrete

    Workability reduces at higher dosage of fibres compared to initial dosage used. Due to more addition of fibres, there is increase in amount of entrapped air voids due to presence of fibres and therefore increase in air content attributes in reducing workability and difficulty is observed in compaction of mixes.

    Failure Shapes

    A load resisting mechanism is better due to triangular cross section of fibres undergo twisting kind of the deformation in 3D fibre orientation than circular cross section. A sufficient bond with matrix is observed during the studies. The fibre pull-out is prevented and fibres mainly failed by breaking. Compared to normal concrete, budging effect is observed for FRC cubes. Also no balling off of concrete indicated the gain of residual strength in concrete.

    Compressive Strength

    The addition of polyester fibres to the mix increased the28 day’s compressive strength of the mix with the dosage of 1.5% by 16% due the confinement provided by fibres. The compressive strength at 1.5% dosage is slightly higher than strength at 2% dosage. Compressive strength increases for all dosage of fibres than normal concrete. Reason is that due to confinement provided by fibre bonding characteristics of concrete increases and hence compressive strength increases with the increases in the fibre content.

    Improvement of Shear Strength using Triangular Shape Fibre in Concrete
    Figure 3: Graph for Compressive Strength at Different Fibre Content

    Split Tensile Strength

    Split tensile test does not give perfect estimation about direct tensile strength due to mixed stress field and fibre orientation but its failure pattern gives fairly good idea about ductility of the material. Failure patterns of splitting tensile test indicate that specimens after first cracking do not separate unlike the concrete failure. Large damage zone is produced due to closely spaced micro cracks surrounding a splitting plane. Fibre bridging action and due to that stress transfer mechanism is responsible for such enhanced ductile failure pattern.

    Improvement of Shear Strength using Triangular Shape Fibre in Concrete
    Figure 4: Graph for Split Tensile Strength at Different Fibre Content

    Flexural Strength

    The flexural strength of the mix with the dosage of 1.5% increases by 21%. Nominal increases remains for all dosage of fibres compared to normal mixes. Minor gain is due to influence of top compression block in specimen, as when specimen is subjected to two-point loading, half depth of uncracked portion is under compression and bottom half is under tension.

    Improvement of Shear Strength using Triangular Shape Fibre in Concrete
    Figure 5: Graph for Flexural Strength at Different Fibre Content

    Shear Strength

    The addition of polyester fibres to the mix increased the shear strength of the mix with the dosage of 0.5% and 2% by 20% and 25% respectively. Addition of fibre reduces the crack spacing, thus indicating a more redistribution of stresses. Plain concrete failed in a very brittle manner, but FRC provided a gradual softening in shear. As the first crack forms, the fibres bridge it, transmitting stresses across the crack surface. In order to enforce further crack opening the applied load has to be increased, which leads to the formation of another crack. This mechanism then repeats until failure.

    Improvement of Shear Strength using Triangular Shape Fibre in Concrete
    Figure 5: Graph for Shear Strength at Different Fibre Content

    Conclusion

    • Inclusion of different fibres content adversely affect flow properties of concrete. For wider application of FRC, careful mix proportioning is highly recommended.
    • Polyester fibres did not disperse properly in the mixing water. Addition of fibres to dry mix was found to be more practical.
    • The presence of fibres in concrete alters the failure mode of material. It is found that the failure mode of plain concrete is mainly due to spalling, while the failure mode of fibre concrete is bulging in transverse directions.
    • Compressive strength of material increases with increasing fibre content. Strength enhancement ranges from 9 % to 16 %. For the material used in this study fibre content of 1.5% by volume of concrete has beneficial effect on strength enhancement.
    • Strength enhancement in splitting tensile strength due to fibre addition varies from 6.5 % to 34%. Its failure pattern gives fairly good idea about ductility of the material. Split tensile strength at 28’days is approximately 50% higher than 7 day’s strength.
    • The addition of fibre has significantly enhanced the performance of beam. During the test it was visually observed that the FRC specimen has grater crack control as demonstrated by reduction in crack widths and crack spacing. The flexural strength increases with increasing fibre content. The maximum increase in flexural strength at 1.5 % fibre content is 27%.
    • The shear strength increases with increasing volume percentage of fibres. This is because of fibres enhances the load carrying capacity of mix. The percentage increase in shear strength of the mix varies from 27 % to 32 %.
    • Different test result indicates that for polyester fibre can effectively be used up to 1.5% fibre content.

    References

    • Bairagi N.K. and Modhera C.D., "Shear Strength reinforced concrete," ICI, Jan-March 2001, pp. 47-52.
    • Balaguru P., and Najm H., "Properties of Fiber Reinforced Structural Lightweight Concrete", ACI Material Journal, V. 101, July-Aug 2004, pp. 281-286.
    • Bentur A. and Mindess S., "Fibre Reinforced Cementitious Composites," 2007, Taylor & Francis, London.
    • Chanh N., "Steel Fiber Reinforced Concrete."
    • Chen Pu - Woei, Chung D. D .L. "A Comparative Study of Concretes Reinforced with Carbon, Polyethylene, and Steel Fibers and Their Improvement by Latex Addition", ACI Material Journal, V. 93, March-April 1996, pp. 129-133.
    • Dave U. V. and Desai Y. M. "Effect of Polypropylene, Polyester and Glass fibres on various strength of ordinary and standard concrete" the first international conference on recent advance in concrete technology, Sep. 2007,Washington D.C. U.S.A.
    • Desai A.K., "Earthquake Resistant Ductile Concrete," NBM & CW, Oct 2007, pp.144-159.
    • Desai A.K., "Study of Beam-Column Joint Using HPC with Polyester Fibre under Cyclic Loading," NBM&CW, Jan.2006, pp.140-144.
    • French C., Kreger M.E. , "High Strength Concrete (HSC) in Seismic Regions," 1998, Framington Hills, ACI, vii, 471
    • Karbhari Vistasp M, "Use of Composites for 21st Century Civil Infrastructure," Computer Methods in Applied Mechanics and Engineering, V.185, 2000, pp.433-454.
    • Li V., Ward R. J. and Hamza A., "Steel and synthetic Fibers as Shear Reinforcement," ACI Material Journal, V.89, Sep-Oct 1992, pp. 499-508.
    • Mirsayah A. and Banthia N., "Shear Strength of Steel Fiber-Reinforced Concrete," ACI Material Journal, V.99, Sep-Oct 2002, pp. 473-479.
    • Nagabhushanam M., Ramakrishnan V. and Vondran G. "Fatigue Strength of Fibrillated Polypropylene Fiber Reinforced Concretes" Transportation Research Record, 1989, No. 1226, pp. 36-47.
    • Parameswaran V.S., "High - Performance Fiber Reinforced Concretes," Indian Concrete Journal, Nov. 1996, pp. 621-627.
    • ACI Committee 544, "Measurement of Properties of Fiber Reinforced concrete."

    NBMCW August 2010

    CURRENTLY ONLINE
    We have 430 guests and no members online

    NBM&CW

    New Building Material & Construction World

    New Building Material & Construction World
    MGS Architecture

    Modern Green Structures & Architecture

    Modern Green Structures & Architecture
    L&ST

    Lifting & Specialized Transport

    Lifting & Specialized Transport
    II&TW

    Indian Infrastructure & Tenders Week

    Indian Infrastructure & Tenders Week