Polypropylene Fiber Reinforced Concrete : An Overview

The capability of durable structure to resist weathering action, chemical attack, abrasion and other degradation processes during its service life with the minimal maintenance is equally important as the capacity of a structure to resist the loads applied on it. Although concrete offers many advantages regarding mechanical characteristics and economic aspects of the construction, the brittle behavior of the material remains a larger handicap for the seismic and other applications where flexible behaviour is essentially required. Recently, however the development of polypropylene fiber-reinforced concrete (PFRC) has provided a technical basis for improving these deficiencies. This paper presents an overview of the effect of polypropylene (PP) fibers on various properties of concrete in fresh and hardened state such as compressive strength, tensile strength, flexural strength, workability, bond strength, fracture properties, creep strain, impact and chloride penetration. The role of fibers in crack prevention has also been discussed.

S. K. Singh, Scientist, Structural Engineering Division, Central Building Research Institute, Roorkee & Honorary Secretary Institute of Engineers, Roorkee

Introduction

Ceramics were the first engineering materials known to mankind and they still constitute the most used materials in terms of weight [1, 2]. Hydraulic cements and cement-based composites including concretes are the main ceramic-based materials. Concrete offers many advantages in the application due to its improved mechanical characteristics, low permeability and higher resistance against chemical and mechanical attacks. Although concrete behavior is governed significantly by its compressive strength, the tensile strength is important with respect to the appearance and durability of concrete. The tensile strength of concrete is relatively much lower. Therefore, fibers are generally introduced to enhance its flexural tensile strength, crack arresting system and post cracking ductile behaviour of basic matrix.

Concrete modification by using polymeric materials has been studied for the past four decades [3]. In general, the reinforcement of brittle building materials with fibers has been known from ancient period such as putting straw into the mud for housing walls or reinforcing mortar using animal hair etc. Many materials like jute, bamboo, coconut, rice husk, cane bagasse, and sawdust as well as synthetic materials such as polyvinyl alcohol, polypropylene (PP), polyethylene, polyamides etc. have also been used for reinforcing the concrete [4,5,6,7,8]. Research and development into new fiber reinforced concrete is going on today as well.

Polypropylene fibers were first suggested as an admixture to concrete in 1965 for the construction of blast resistant buildings for the US Corps of Engineers. The fiber has subsequently been improved further and at present it is used either as short discontinuous fibrillated material for production of fiber reinforced concrete or a continuous mat for production of thin sheet components. Since then the use of these fibers has increased tremendously in construction of structures because addition of fibers in concrete improves the toughness, flexural strength, tensile strength and impact strength as well as failure mode of concrete. Polypropylene twine is cheap, abundantly available, and like all manmade fibers of a consistent quality.

Properties of Polypropylene Fibers

The raw material of polypropylene is derived from monomeric C3H6 which is purely hydrocarbon. Its mode of polymerization, its high molecular weight and the way it is processed into fibers combine to give polypropylene fibers very useful properties as explained below [9]:
Polypropylene Fiber Reinforced Concrete Polypropylene Fiber Reinforced Concrete
Figure 1: monofilament fiber Figure 2: Fibrillated fiber
The fibers are manufactured either by the pulling wire procedure with circular cross section or by extruding the plastic film with rectangular cross-section. They appear either as fibrillated bundles, mono filament or microfilaments as shown in Fig. 1 & 2. The properties of these three types of PP fibers are given in Table 1 [10]. The fibrillated polypropylene fibers are formed by expansion of a plastic film, which is separated into strips and then slit. The fiber bundles are cut into specified lengths and fibrillated. In monofilament fibers, the addition of buttons at the ends of the fiber increases the pull out load. Further, the maximum load and stress transfer could also be achieved by twisting fibers [11].

Role of Fibers

Cracks play an important role as they change concrete structures into permeable elements and consequently with a high risk of corrosion. Cracks not only reduce the quality of concrete and make it aesthetically unacceptable but also make structures out of service. If these cracks do not exceed a certain width, they are neither harmful to a structure nor to its serviceability. Therefore, it is important to reduce the crack width and this can be achieved by adding polypropylene fibers to concrete [13]. The bridging of cracks by the addition of PP fibers has been shown in Fig 3.

Thus addition of fibers in cement concrete matrix bridges these cracks and restrains them from further opening. In order to achieve more deflection in the beam, additional forces and energies are required to pull out or fracture the fibres. This process, apart from preserving the integrity of concrete, improves the load-carrying capacity of structural member beyond cracking. This improvement creates a long post-peak descending portion in the load deflection curve as shown in Fig 4 [12]. Reinforcing steel bars in concrete have the same beneficial effect because they act as long continuous fibres. Short discontinuous fibres have the advantage, however, of being uniformly mixed and dispersed throughout the concrete.

The major reasons for crack formation are Plastic shrinkage, Plastic settlement, Freeze thaw damage, Fire damage etc.

Plastic shrinkage: It occurs when surface water evaporates before the bleed water reaches the surface. Polypropylene fibers reduce the plastic shrinkage crack area due to their flexibility and ability to conform to form. The addition of 0.1% by volume of fibers is found effective in reducing the extent of cracking by a factor of 5-10. The extent of crack reduction is proportional to the fiber content in the concrete.

Table 1: Properties of various types of polypropylene fibers
Fiber type Length (mm) Diameter (mm) Tensile strength (MPa) Modulus of elasticity (GPa) Specific surface (m2/kg) Density (kg/cm3)
monofilament 30-50 0.30-0.35 547-658 3.50-7.50 91 0.9
microfilament 12-20 0.05-0.20 330-414 3.70-5.50 225 0.91
Fibrillated 19-40 0.20-0.30 500-750 5.00-10.00 58 0.95

Polypropylene Fiber Reinforced Concrete
Figure 3: Bridging of crack using Polypropylene fibers Figure 4: Typical load-elongation response in tension of FRC.

Plastic settlement: High rate of bleeding and settlement combined with restraint to settlement (e.g. by reinforcing bars) leads to settlement cracking. In case of PFRC, fibers are uniformly distributed. Fibers are flexible so they cause negligible restraint to settlement of aggregates.

Freeze thaw damage: Small addition of polypropylene fibers in concrete reduces the flow of water through the concrete matrix by preventing the transmission of water through the normal modes of ingress, e.g. capillaries, pore structure, etc. The implications of these qualities in concrete with polypropylene fiber additions are that cement hydration will be improved, separation of aggregate will be reduced and the flow of water through concrete that causes deterioration from freeze/ thaw action and rebar corrosion will be reduced, creating an environment in which enhanced durability may take place.

Polypropylene Fiber Reinforced Concrete
Spalling of homogenous structure of Concrete due to insufficient capillary pores Developed explosion channels due to melting of PP fibers
Figure 5: Flowing out of steam pressure through the melted PP fibers in the case of fire

Fire damage: Heat penetrates the concrete resulting in desorption of moisture in outer layer. Moisture vapors flow back towards the cold interior and are reabsorbed into voids. Water and vapor accumulate in the interior thereby increasing the vapor pressure rapidly causing cracks and spalling in the concrete. In case of PFRC, the fibers melt at 160oC creating voids in the concrete. The vapor pressure is released in newly formed voids and explosive spalling is significantly reduced as shown in fig 5[14].

Properties of PP Fiber Reinforced Concrete

Before mixing the concrete, the fiber length, amount and design mix variables are adjusted to prevent the fibers from balling. Good FRC mixes usually contain a high mortar volume as compared to conventional concrete mixes. The aspect ratio for the fibers are usually restricted between 100 and 200 since fibers which are too long tend to "ball" in the mix and create workability problems. As a rule, fibers are generally randomly distributed in the concrete; however, placing of concrete should be in such a manner that the fibers become aligned in the direction of applied stress which will result in even greater tensile and flexural strengths. There should be sufficient compaction so that the fresh concrete flows satisfactorily and the PP fibers are uniformly dispersed in the mixture. The fibers should not float to the surface nor sink to the bottom in the fresh concrete. Chemical admixtures are added to fiber-reinforced concrete mixes primarily to increase the workability of the mix. Air-entraining agents and water-reducing admixtu- res are usually added to mixes with a fine aggregate content of 50% or more. Superplasticizers, when added to fiber-reinforced concrete, can lower water: cement ratios, and improve the strength, volumetric stability and handling characteristics of the wet mix. The properties of PFRC with various fiber volume % are shown in Table 2.

Table 2 Mechanical Properties of Polypropylene Fiber Reinforced Concrete
No Concrete mix Fibers Vf % fcu (MPa) ft (MPa) fs (MPa) Slump (mm) Ref.
w/c Cement (kg/m3) CA (kg/m3) FA (kg/m3) Admixture Specimen shape Type l/d
1. 0.49 390 (OPC) 1000 (10mm) 640 Super plasticizer (Fosroc 430) Cylinder, Cubes & Prism Fibrillated
(20mm long & 0.29mm dia)
69 0 0.10 0.30 17.2 14.1
12.6
1.08 1.72 1.34 4.5
2.5
3.0
100 – 120 [15]
2. 0.45 360 (OPC) 1100 (20mm) 647 - Prism Micro filament
(19mm long & 0.048mm dia)
396 0 0.045 0.082 0.128 - -
-
-
2.24 2.33
2.40
2.43
4.01 3.76 4.01 4.22 - -
-
-
[10]
3. 0.45 360 (OPC) 1100 (20mm) 647 - Prism Mono filament
(30mm long & 0.55 mm dia)
55 1.0 1.2 1.4 - -
-
2.50
2.68
2.70
5.36 5.47 5.51 -
-
-
[10]
4. 0.48 418 (OPC) 724 (25mm) 998 - Cylinder Mono filament 56 0 1.0 1.5 35.03
35.42
30.74
2.23 3.21 3.21 - - - 102
38
7
[16]
5. 0.40 372 OPC + 28 SF 1140
(20mm)
750 Super-plasticizer Prism Mono filament 200 0 0.5 56.10
56.10
4.10 4.40 5.21
5.61
100
80
[29]
6. 0.50 383
(PPC)
1162
(20mm)
572 - Cylinder, Cubes & Prism Graded Fibrillated (12mm ~ 24mm) NR 0 0.1 0.2 0.3 35.23
39.50
41.00
48.00
3.54 4.42 4.88 4.95 5.23
5.47
5.65
6.35
- -
-
-
[25]
7. 0.44 430
(PPC)
1154
(20mm)
540 - Cylinder, Cubes & Prism Graded Fibrillated
12mm ~ 24mm)
NR 0 0.1 0.2 0.3 41.22
49.78
50.22
52.00
3.72 4.53 4.67 4.75 5.35
5.99
6.12
6.29
- -
-
-
[25]
8. 0.39 498
(PPC)
1136
(20mm)
503 NIL Cylinder, Cubes & Prism Graded Fibrillated
12mm ~ 24mm)
NR 0 0.1 0.2 0.3 46.15
50.67
55.33
57.11
3.89 4.88 5.09 5.52 5.56
5.70
6. 40
6.84
- -
-
-
[25]
9. 0.30 567
(OPC)
630 1050 Superplasticizer
(Paric FP300U)
Cylinder Fibrillated
(6 mm long & 0.06 mm dia)
100 0 0.25 0.50 81.60
60.80 60.00
4.40
4.10
4.30
- -
-
400-600 [23]
10. 0.30 567
(OPC)
630 1050 Superplasticizer
(Paric FP300U)
Cylinder Fibrillated(30mm long& 0.06mm di) 500 0.25 0.50 71.90
59.40
5.40
4.70
- - 400-600 [23]
11. 0.36 314OPC+56 Fly ash 1268 (20mm) 713 Super plasticizer Cylinder, Cubes & Prism -
Mono filament
Mesh Type
-
700
150
0 0.10 0.10 38.20
37.60
37.20
-
-
-
4.80
5.10
5.40
73 55
45
[30]
12. 0.40 415 1120
(20mm)
740 - Cubes & Cylinder Fibrillated 126 0
0.1
0.2
0.3
38.0
34.5
42.0
41.4
4.00
4.40
5.00
5.15
- -
-
-
20
20
15
10
[28]
Where: Vf - volume fraction of fiber; fcu - compressive strength; ft - tensile strength and fs - flexural strength, SF- Silica fume

Polypropylene fibers are used in two different ways to reinforce cementitious matrices. One application is in thin sheet components in which polypropylene provides the primary reinforcement. Its volume content is relatively high exceeding 5%, in order to obtain both strengthening and toughening. In other application the volume content of the polypropylene is low, less than 0.3% by volume, and it is intended to act mainly as secondary reinforcement for crack control, but not for structural load bearing applications [11]. The performance and influence of the polypropylene fibers in the fresh and hardened concrete is different and therefore these two topics are treated separately.

Effects on Fresh Concrete
The main parameter, which is often used to determine the workability of fresh concrete, is the slump test. The slump value depends mainly on the water absorption and porosity of the aggregates, water content in the mixture, amount of the aggregate and fine material in the mixture, shape of the aggregates and surface characteristics of the constituents in the mixture. The slump values decrease significantly with the addition of polypropylene fibers as shown in Table 3. The concrete mixture becomes rather clingy resulting in increasing of the adhesion and cohesiveness of fresh concrete. During mixing the movement of aggregates shears the fibrillated fibers apart, so that they open into a network of linked fiber filaments and individual fibers. These fibers anchor mechanically to the cement paste because of their large specific surface area. The concrete mixture with polypropylene fibers results in the fewer rate of bleeding and segregation as compared to plain concrete. This is because the fibers hold the concrete together and thus slow down the settlement of aggregates. Due to its high tensile and pull-out strength, the PP fibers even reduce the early plastic shrinkage cracking by enhancing the tensile capacity of fresh concrete to resist the tensile stresses caused by the typical volume changes. The fibers also distribute these tensile stresses more evenly throughout the concrete. As the plastic shrinkage cracking decreases, the number of cracks in the concrete under loading is reduced, due to decrease in cracks from the existing shrinkage cracks. If shrinkage cracks are still formed, the fibers bridge these cracks, reducing at the same time their length and width. Moreover, as the rate of bleeding decreases, the use of polypropylene fibers may accelerate the time to initial and final set of the concrete as this led to a slower rate of drying in the concrete [14].

Table 3: Effect of polypropylene fibers on concrete slump [18]
(mm)
Initial slump
(mm)
Final slump
(mm)
Fiber length
(mm)
90
130
170
127
1245
114
76
70
120
48
53
64
51
51
30
51
51
19

Effects on Hardened Concrete
The addition of polypropylene fibres in the concrete did not significantly affect the compressive strength and the modulus of elasticity but they do increase the tensile strength. Splitting tensile strength of PFRC approx ranges from 9% to 13% of its compressive strength. Addition of PP fibers in concrete increases the splitting tensile strength by approx 20% to 50% [16].

Compressive strength: The compression strength of concrete is a vital parameter as it decides the other parameters like tension, flexure etc. The effect of polypropylene fiber on the compressive strength of concrete has been discussed in many literatures and observed that polypropylene fiber either decreases or increases the compressive strength of concrete, but overall effect is negligible in many cases. In fact, the effect of a low volume of polypropylene fiber on the compressive strength of concrete may be concealed by the experimental error.

Flexural tensile strength: The flexural tensile strength increases with increase in volume fraction of fiber. It is also observed that there was increase in strength for with the increase in aspect ratio of fibre.

Polypropylene Fiber Reinforced Concrete Polypropylene Fiber Reinforced Concrete
Figure 6: Fracture shape of plain concrete Figure 7: Fracture shape of PFR concrete
Bond strength: It is necessary that there should be a good bond between the fiber and the matrix. If the critical fiber volume for strengthening has been reached then it is possible to achieve multiple cracking. This is a desirable situation because it changes a basically brittle material with a single fracture surface to fracture into a pseudo ductile material which can absorb transient minor overload and shocks with little visible damage. So the aim is to produce large number of multiple cracks at as close spacing as possible so that the crack widths are very small, almost invisible to naked eye so that the rate at which aggressive materials can penetrate the matrix is reduced. High bond strength helps to give close crack spacing but it is also essential that the fibers should give sufficient ductility to absorb impacts. But in terms of physiochemical adhesion there is no bond between the fiber and the cement gel. The use of chopped and twisted fibrillated polypropylene fibers with their open structure has partially remedied the lack of interfacial adhesion by making use of wedge action at the slightly open fiber ends and also by mechanical bonding through fibrillation. The general pull out loads of twisted fibrillated fibers [20, 21] may range from 300-500N for commonly used staples but the accurate calculation of bond strength is complicated by a lack of knowledge of the surface area of fiber in contact with the paste. It is observed that in damaged products and in broken specimens, usually fiber breaks instead of fiber pull out [9].

Fracture Properties: The failure behaviour of high-strength concretes is effectively improved by the use of fibers. The typical shear bond rupture due to strain localization could be avoided (fig. 6). Instead of this, a large number of the longitudinal cracking, which was predominantly oriented in the direction parallel or sub-parallel to the external compressive stresses, was formed at the entire concrete specimens as shown in fig7.

Creep and shrinkage properties of concrete: Fibers reduce creep strain, which is defined as the time-dependent deformation of concrete under a constant stress. Compressive creep values, however, may be only 10 to 20% of those for normal concrete. Shrinkage of concrete, which is caused by the withdrawal of water from concrete during drying, is also reduced by fibers. The shrinkage, creep and total time dependent deformation of various PFRC mixes along with non fibrous concrete mix are presented in fig 8[15]. The reduction in shrinkage due to the presence of fibers is expected from number of viewpoints. First, the fibers do not exhibit any shrinkage, thus reducing overall shrinkage of the mix. In addition the fibers have a role in retaining the water in the concrete mix upto a certain limit which helps to delay the shrinkage. Therefore addition of fibers to the concrete mixes is always advantageous in reducing shrinkage deformation.

Polypropylene Fiber Reinforced Concrete Polypropylene Fiber Reinforced Concrete
Figure 8: Time dependent deformation of polypropylene fibers Figure10: Effect of polypropylene fibers on impact resistance of concrete

Flexural impact properties: The number of blows required to develop the first visible crack on the beam’s lower surface is defined as the initial-crack impact number (Ncr). Failure impact number Nf is defined as the number at which one main macro-crack develops from bottom to top of the beam. Impact ductility index is defined as the ratio of failure impact number to initial crack impact number, which can be used to present the flexural impact ductility.

J=Nf / Ncr

where J is impact ductility index, which for plain concrete is 1. The flexural impact test results are shown in table 6 by researcher[10]. The impact resistance for concretes with various volume fractions of fibrillated polypropylene fibers has been shown in figure 10. The results indicate that significant improvement in impact resistance of concrete can be achieved with relatively low volume fraction of polypropylene fibers.

Table 6: Impact properties of fiber reinforced concrete
Type of mix Vf % Average Impact number Average failure
Impact number
Impact ductility index
Control 0 25.8 26.8 1.04
Microfilament 0.05
0.095
0.14
34.7
28.6
38.1
46.5
30.4
40.1
1.34
1.06
1.05
Monofilament 1
1.2
1.4
68.9
70.7
62.8
224.2
712.7
831
3.26
10.08
13.23

Chloride penetration: Besides improved mechanical properties due to inclusion of fiber, chloride penetration is also reduced substantially by the presence of fibers depending upon its orientation. Antoni [17] studied the effect of chloride penetration and found that the effect is insignificant for shorter fiber due to the random orientation of short fibers as compare to long fibers. Further, the chloride movement into concrete is reduced significantly by the presence of fiber as the interfacial transition zone in the direction perpendicular to the chloride penetration whereas fiber provides easier path for the chloride to migrate in direction along the fiber.

Obstacles in Use of PFRC

Although PP fibers are gaining wide applications in many fields, there is still need for improvement in some properties. A major fire will leave the concrete with additional porosity equal to the volume of fibers incorporated in the concrete usually in the order of 0.3 to 1.5% by volumetric fraction. In respect of monofilament fibers, the poor bond between fiber and matrix results in a low pull out strength. The PP fibers are also attacked by sunlight and oxygen, however surrounding concrete in PFRC protects the fibers so well that this shortcoming is not significant. Further, sometimes the fibers function as initiator of the micro cracking because of their low modulus of elasticity as compared to the cement matrix. Thus mechanical bond with the cement matrix is also low. The fibers cause the enhancement of the pores volume of concrete by creating more micro-defects in the cement matrix.

Conclusion

Innovations in engineering design and construction, which often call for new building materials, have made polypropylene fiber-reinforced concrete applications. In the past several years, an increasing number of constructions have been taken place with concrete containing polypropylene fibres such as foundation piles, prestressed piles, piers, highways, industrial floors, bridge decks, facing panels, flotation units for walkways, heavyweight coatings for underwater pipe etc. This has also been used for controlling shrinkage & temperature cracking.

Due to enhance performances and effective cost-benefit ratio, the use of polypropylene fibers is often recommended for concrete structures recently. PFRC is easy to place, compact, finish, pump and it reduces the rebound effect in sprayed concrete applications by increasing cohesiveness of wet concrete. Being wholly synthetic there is no corrosion risk. PFRC shows improved impact resistance as compared to conventionally reinforced brittle concrete. The use of PFRC provides a safer working environment and improves abrasion resistance in concrete floors by controlling the bleeding while the concrete is in plastic stage. The possibility of increased tensile strength and impact resistance offers potential reductions in the weight and thickness of structural components and should also reduce the damage resulting from shipping and handling.

Acknowledgment
The author wishes to express his sincere thanks to Ms Sonal Dhanvijay & Ms Vedanti Ganwir of Visvesvaraya National Institute of Technology, Nagpur for their valuable help in preparing this paper.

References

NBM&CW December 2011
Click Here
To Know More or to Contact the Manufacturer
Accelerated Building & Bridge Construction with UHPC

Accelerated Building & Bridge Construction with UHPC

UHPC, which stands for Ultra High-Performance Concrete, is a testament to the ever-evolving panorama of construction materials, promising unparalleled strength, durability, and versatility; in fact, the word concrete itself is a misnomer

Read more ...

Innovative Approaches Driving Sustainable Concrete Solutions

Innovative Approaches Driving Sustainable Concrete Solutions

This paper explores the evolving landscape of sustainable concrete construction, focusing on emerging trends, innovative technologies, and materials poised to reshape the industry. Highlighted areas include the potential of green concrete

Read more ...

GGBS: Partial Replacement Of Cement For Developing Low Carbon Concrete

GGBS: Partial Replacement Of Cement For Developing Low Carbon Concrete

Dr. L R Manjunatha, Vice President, and Ajay Mandhaniya, Concrete Technologist, JSW Cement Limited, present a Case Study on using GGBS as partial replacements of cement for developing Low Carbon Concretes (LCC) for a new Education University

Read more ...

Behaviour of Ternary Concrete with Flyash & GGBS

Behaviour of Ternary Concrete with Flyash & GGBS

Evaluating the performance of concrete containing Supplementary Cementitious Materials (SCM) like FlyAsh and Ground Granulated Blast Furnace Slag (GGBS) that can be used in the production of long-lasting concrete composites.

Read more ...

Nanospan’s Spanocrete®: nano-admixture for concrete

Nanospan’s Spanocrete®: nano-admixture for concrete

Nanospan’s Spanocrete, a Greenpro-certified, award- winning, groundbreaking nano-admixture for concrete, actualizes the concept of “durability meets sustainability”. This product simplifies the production of durable concrete, making it cost-effective

Read more ...

The Underwater Concrete Market in India

The Underwater Concrete Market in India

India, with its vast coastline and ambitious infrastructural projects, has emerged as a hotspot for the underwater concrete market. This specialized sector plays a crucial role in the construction of marine structures like bridges, ports

Read more ...

The Path to Enhanced Durability & Resilience of Concrete Structures

The Path to Enhanced Durability & Resilience of Concrete Structures

This article highlights a comprehensive exploration of the strategies, innovations, and practices for achieving concrete structures that not only withstand the test of time but also thrive in the face of adversity.

Read more ...

Self-Curing Concrete for the Indian Construction Industry

Self-Curing Concrete for the Indian Construction Industry

The desired performance of concrete in the long run depends on the extent and effectiveness of curing [1 & 2]. In the Indian construction sector, curing concrete at an early age is a problematic issue because of lack of awareness or other

Read more ...

BigBloc Construction an emerging leader in AAC Block

BigBloc Construction an emerging leader in AAC Block

Incorporated in 2015, BigBloc Construction Ltd is one of the largest and only listed company in the AAC Block space with an installed capacity of 8.25 lakh cbm per annum. The company’s manufacturing plants are located in Umargaon

Read more ...

Decarbonizing Cement Industry: Sustainable & Energy-Efficient Measures

Decarbonizing Cement Industry: Sustainable & Energy-Efficient Measures

Dr. L R Manjunatha (VP), Manoj Rustagi (Chief Sustainability & Innovation Officer), Gayatri Joshi (ASM), and Monika Shrivastava (Head of Sustainability) at JSW Cement Limited, discuss new approaches for Decarbonizing the Cement

Read more ...

Concrete Rheology: Technology to Describe Flow Properties of Concrete

Concrete Rheology: Technology to Describe Flow Properties of Concrete

Concrete is a heterogeneous composite complex material, and its hardened property is influenced by its fresh property. Concrete today has transformed into an advanced type with new and innovative ingredients added - either singly or in

Read more ...

Amazecrete ICRETE: Making Concrete Economical & Durable

Amazecrete ICRETE: Making Concrete Economical & Durable

ICRETE offers many benefits apart from reducing cement content and giving high grades saving to ready-mix concrete companies; it helps reduce shrinkage and permeability in concrete slabs, increases the durability of concrete, and also works

Read more ...

UltraTech Cement & Coolbrook’s RotoDynamic HeaterTM Technology

UltraTech Cement & Coolbrook’s RotoDynamic HeaterTM Technology

UltraTech Cement Limited, India’s largest cement and ready-mix concrete (RMC) company, and Coolbrook, a transformational technology and engineering company, will jointly develop a project to implement Coolbrook’s RotoDynamic HeaterTM (RDH)

Read more ...

Plastic Shrinkage and Cracks in Concrete

Plastic Shrinkage and Cracks in Concrete

Plastic shrinkage cracking occurs when fresh concrete is subjected to a very rapid loss of moisture. It is caused by a combination of factors such as air and concrete temperature, relative humidity, and wind velocity at the surface of concrete. These can cause

Read more ...

Dam Rehabilitation With Cutoff Wall for Seepage Control

Dam Rehabilitation With Cutoff Wall for Seepage Control

This paper covers the research work carried out on cement plastering process for internal and external building wall by using spray plastering machine. Objective of study is to experiment and compare the plastering activity by conventional way and

Read more ...

Construction Defects Investigation & Remedies

Construction Defects Investigation & Remedies

In recent years, the speed of construction has increased very fast; buildings which used to take 3-5 years are now getting completed in 1-2 years. There is a race to complete projects faster, but due to this speedy construction, the quality of construction is often

Read more ...

Challenges in usage of Hydrogen in Cement Industry

Challenges in usage of Hydrogen in Cement Industry

With its zero-emission characteristics, hydrogen has become a promising decarbonization path for the cement industry. While there are several issues that need to be resolved in the use of hydrogen, there are also many advantages, so much so that the growth

Read more ...

Enhancing Corrosion Resistance of Steel Bars in Reinforced Concrete Structures

Enhancing Corrosion Resistance of Steel Bars in Reinforced Concrete Structures

Reinforced concrete is a composite material which is made using concrete and steel bars. Concrete takes the compressive forces and steel bar takes tensile forces. Concrete around the steel bar protects it from corrosion by providing an alkaline environment

Read more ...

Moving toward workability retention to rheology retention with low viscosity concrete technology

Moving toward workability retention to rheology retention with low viscosity concrete technology

Amol Patil, Sr. Specialist - General Manager (Admixture and Specialty Products), Master Builders Solutions (India), and Nilotpol KAR, Managing Director, Master Builders Solutions (South Asia), present a paper on the concept of low viscosity concrete in

Read more ...

Cement industry innovating eco-friendly packaging

Cement industry innovating eco-friendly packaging

Cement companies are constantly innovating to meet global sustainability standards and improve logistics, shelf life, and utility of cement, while reducing wastage. Thei aim is to reduce their environmental impact without compromising their product